One Year Clinical Evaluation of Milled BioHPP Polyetheretherketone (PEEK)-Based versus Metal Ceramic Single Crowns (Randomized Controlled Clinical Trial) / Avaliação Clínica de um Ano de Coroas Fresadas à Base de Biohpp Polieteretercetona (PEEK) Versus Coroas Metalocerâmicas Unitárias (Ensaio Clínico Controlado Randomizado)

Objective: To evaluate the clinical behavior of milled BioHPP PEEK copings veneered with Visio.lign composite resin in comparison with metal copings veneered with feldspathic porcelain as single posterior crowns. Material and Methods: Twenty Four full coverage posterior crowns were fabricated for endodontically treated molars divided into 2 groups according to the material used. Twelve milled BioHPP PEEK-based crowns (Group 1) and Twelve Porcelain Fused to Metal (PFM) crowns (Group 2). The preparations were standardized with an equi-gingival, deep chamfer finish line for all teeth. BioHPP PEEK and metal copings were fabricated by CAD/CAM technology and lost wax technique respectively. These coping were veneered according to manufactures instructions either by special composite resin or low fusing glass ceramic respectively. The restorations were cemented then clinical evaluation of these crowns was assessed regarding mechanical failure, marginal integrity and patient satisfaction every two months for one year. Results: Although two PEEK crowns were fractured, both PEEK and PFM crowns showed similar fracture (mechanical failure) and marginal integrity without significant difference (p > 0.05). BioHPP PEEK-based crowns showed statistically significantly lower patient satisfaction than PFM crowns after six months (p-value = 0.013, Effect size = 1.157) but all the patients were generally satisfied. Conclusion: BioHPP PEEK-based crowns showed clinically similar and accepted mechanical behavior and marginal integrity but less patient's satisfaction than PFM crowns after six months. So BioHPP PEEK-based crowns may be used as an alternative tooth-colored metal-free fixed restoration for one year (AU)

Objetivo: Avaliar o comportamento clínico de copings fresados de BioHPP PEEK com cobertura de resina composta Visio.lign em comparação com copings metálicos cobertos com cerâmica feldspática em coroas unitárias posteriores. Material e Métodos: Vinte e quatro coroas totais posteriores de foram confeccionadas para molares tratados endodonticamente e divididos em 2 grupos de acordo com o material utilizado. Doze coroas fresadas à base de BioHPP PEEK (Grupo 1) e doze coroas de porcelana fundida ao metal (PFM) (Grupo 2). Os preparos foram padronizados para todos os dentes com término de chanfro largo ao nível gengival. BioHPP PEEK e os copings metálicos foram fabricados por tecnologia CAD/CAM e técnica da cera perdida, respectivamente. A aplicação da cobertura sobre os copings foi realizada de acordo com as instruções do fabricante, por resina composta especial ou cerâmica vítrea de baixa fusão, respectivamente. As restaurações foram cimentadas e a avaliação clínica dessas coroas foi realizada quanto à falha mecânica, integridade marginal e satisfação do paciente a cada dois meses durante um ano. Resultados: Embora duas coroas de PEEK tenham sido fraturadas, ambas as coroas de PEEK e PFM apresentaram fraturas semelhantes (falha mecânica) e integridade marginal sem diferença significativa (p > 0,05). As coroas à base de BioHPP PEEK mostraram uma satisfação do paciente significativamente menor do que as coroas PFM após seis meses (valor de p = 0,013; tamanho do efeito = 1,157), mas todos os pacientes estavam geralmente satisfeitos. Conclusão: As coroas à base de BioHPP PEEK, em comparação às coroas PFM, mostraram desempenho clínico similar, aceitável comportamento mecânico e integridade marginal, mas menos satisfação do paciente, após seis meses. Portanto, as coroas à base de BioHPP PEEK podem ser utilizadas como uma alternativa de restauração livre de metal semelhante à cor do dente, por um ano. (AU)

Reabilitação com coroas metal free em dentes anteriores traumatizados e com rizogênese incompleta: relato de caso / Rehabilitation with metal free crowns in traumatized anterior teeth with incomplete rhizogenesis: case report

Objetivo: rizogênese incompleta refere-se a dentes permanentes em que não houve a formação completa do ápice radicular, ocasionando perda da vitalidade pulpar e, consequentemente, incapacidade da bainha epitelial de Hertwig para induzir a formação completa da raiz. Devido ao traumatismo e escurecimento dental, se faz necessário em certos casos a confecção de coroas em porcelana pura para reabilitar a paciente em estética e função. O presente trabalho tem como objetivo demonstrar um caso de reabilitação estética e funcional em dente com rizogênese incompleta, onde se consideraram as perdas estruturais e alteração de cor, para que seja possível estabelecer o tratamento mais adequado. Relato de caso: paciente de 16 anos, gênero feminino, atendida na Clínica de Odontologia de uma instituição privada, insatisfeita com a estética do seu dente devido ao escurecimento do elemento 21, pois quando tinha 5 anos o dente foi traumatizado juntamente com o elemento 11. O plano de tratamento adotado para ambos os elementos foi a confecção de peças protéticas em porcelana e cimentação. Considerações finais: esse caso demonstrou que a confecção de coroas estéticas em porcelana é considerada uma boa conduta na rotina clínica em casos de escurecimento dental, devolvendo estética e função para o paciente.(AU)

Objective: incomplete rhizogenesis refers to permanent teeth with incomplete formation of the root apex, causing loss of pulp vitality and the consequent inability of the Hertwig epithelial sheath to induce complete root formation. Due to dental trauma and darkening, some cases require the production of pure porcelain crowns to rehabilitate the aesthetics and function of patients. The present study aims to show a case of aesthetic and functional rehabilitation in a tooth with incomplete rhizogenesis, in which structural losses and color change were considered to establish the most appropriate treatment. Case report: a 16-year-old female patient treated at the Dental Clinic of a private institution. The patient was not satisfied with the aesthetics of her tooth due to the darkening of element 21, because at 5 years old the tooth was traumatized along with element 11. The treatment used for both elements was the production of prosthetic porcelain crowns and cementation. Final considerations: this case showed that the production of aesthetic porcelain crowns is considered a good conduct in the clinical routine in cases of tooth darkening, returning aesthetics and function to the patient.(AU)

Diferentes sistemas cerâmicos na reabilitação oral: relato de caso clínico / Ceramic systems different in oral rehabilitation: case report

O objetivo deste trabalho é apresentar um caso clínico, demonstrando a associação entre diferentes tipos de restaurações e sistemas cerâmicos, na reabilitação do sorriso de uma paciente do gênero feminino com queixas em relação à cor e ao posicionamento dos elementos anteriores superiores. Ao exame clínico constatou-se exposição do metal da coroa metalocerâmica no elemento 21 e escurecimento, mau posicionamento dos elementos 13, 12, 22 e 23, além de diferença de cor entre os dentes. Foi proposto como plano de tratamento a substituição das coroas metalocerâmicas por novas coroas nos elementos 11 e 21, e a confecção de facetas indiretas em cerâmica reforçada por dissilicato de lítio (IPS e-max Press, Ivoclar Vivadent) nos dentes 13, 12, 22 e 23. A associação entre coroas metalocerâmicas e facetas convencionais, mostrou-se uma forma de tratamento efetiva na reabilitação do sorriso, garantindo ao final do tratamento correta seleção de cor, boa adaptação marginal das restaurações, alinhamento adequado e também, bons resultados estéticos e boa função mastigatória, contribuindo para a satisfação da paciente.

The aim of this study is to present a clinical case demonstrating the association between different types of restorations and ceramic systems in the smile rehabilitation of a female patient with complaints about the color and and placement of the maxillary anterior elements. On clinical examination it was found metal exposure of the metal-ceramic crown on element 21, darkening and poor positioning of elements 13,12, 22 and 23, as well as, color difference between the teeth. Was proposed as treatment plan the replacement of metal-ceramic crowns by new crowns in the elements 11 e 21, and the making of indirect veneers in ceramic reinforced by lithium dissilicate (IPS e-max Press, Ivoclar Vivadent) on teeth 13, 12, 22 and 23. The association between metal-ceramic crowns and conventional veneers, proved to be a form of effective treatment in the smile rehabilitation, ensuring in the end of the treatment correct color selection, good marginal adaptation of restorations, proper alignment and also good esthetic results and good chewing function , contributing to patient satisfaction.

Degradação Adesiva de um Compósito Auto Aderente aos Substratos da Técnica Indireta / Bonding Degradation of a Self-Adhering Composite to Substrates used in Indirect Technique

O objetivo desse estudo foi avaliar a resistência de união - RU ao cisalhamento de um compósito fluido auto aderente em quatro substratos utilizados na técnica indireta, com uma semana e um ano de armazenamento em água destilada. Quarenta e oito amostras (5 mm largura / 15 mm comprimento / 2 mm espessura) foram preparadas em laboratório protético: 12 amostras do(a) cerômero Adoro/AD, cerâmica/leucita Empress Esthetic/EE, cerâmica/zircônia ZirCAD/ZI (Ivoclar Vivadent), mais a liga Fit Cast SB/ME (Talladium do Brasil), sendo as amostras divididas em dois grupos para cada período de tempo (uma semana e um ano). Dois compósitos fluidos (Controle / FF-Filtek Z350XT Flow / 3M ESPE e o auto aderente / DF-Dyad Flow / Kerr) foram unidos aos quatro substratos. Quatro matrizes Tygon foram posicionadas sobre as amostras, as quais foram preenchidas com os compósitos FF e DF (fotopolimerização 20s). As matrizes foram removidas para expor os corpos de prova (12 por grupo) e as amostras foram armazenadas em água destilada/ 37±2 °C por uma semana e um ano. Após estes períodos, cada amostra foi conectada a uma máquina de ensaios para realização dos ensaios de RU a uma velocidade de 1,0 mm/min, até a falha. Os resultados foram analisados por ANOVA e teste de Tukey (p<0,05). Nos ensaios de uma semana, os substratos leucita e metal apresentaram as maiores médias de RU para ambos os compósitos. Nos ensaios de um ano, os substratos não apresentaram diferença estatística nas médias de RU para ambos os compósitos, com exceção da zircônia que apresentou resultado nulo. Os valores médios de RU, no entanto, foram significativamente menores quando comparados com os resultados dos ensaios de uma semana.(AU)

The aim of this study was to evaluate the shear bond strength (SBS) of a self-adhering flowable composite on four substrates used in indirect technique, for a week and one year of storage in distilled water. Forty eight samples (5 mm wide / 15 mm length / 2 mm thick) were prepared at dental prosthetic laboratory: 12 samples of the ceromer Adoro/AD, leucite ceramic IPS Empress Esthetic/EE, zirconia ceramic ZirCAD/ZI (Ivoclar Vivadent) and the metal ceramic alloy Fit Cast SB/ME (Talladium do Brasil). Samples of each substrate were divided into two groups for each time (a week and one year). Two flowable composites (Control/FF-Filtek Z350 XT Flow/3M ESPE, and the self-adhering/DF-Dyad Flow/Kerr) were bonded to four substrates. Four Tygon tubing were positioned over each sample, which were filled in with the composites FF and DF, and visible light-cured for 20s. The tubings were removed to expose the specimens (12 per group) in format of cylinders, and the samples were stored in distilled water at 37 ± 2°C for one week and one year. After these periods, each sample was attached to testing machine and the specimens were submitted to the shear bond strength test at speed of 1.0mm/min, until failure. The results were analyzed by ANOVA and Tukey test (p<0.05). To one week tests, the substrates leucite and metal showed the highest SBS means, to both composites. For the one-year experiments, the substrates did not show differences in the SBS averages for both composites, except for zirconia that showed null result. However, the SBS averages were lower when compared to one week tests.(AU)

Fracturing of revision of a cobalt-chrome femoral head after fracturing of a ceramic femoral head, with diffuse metallosis. Case report

We presente a case of a fracture of a cobalt-chrome femoral head after revision of a hip total prosthesis with ceramic femoral head fracture. During surgery we found the cobalt-chrome femoral head fracture, wear of the polyethylene and massive metallosis in muscular and cartilaginous tissue. Both femoral stem and acetabular cup were stable and without apparent wearing. After surgical debridement, we promoted the substitution of the femoral head and the acetabular polyethylene by similar ones. After 12 months of follow-up, the patient has no pain complaints, function limit or systemic signs associated with malign metallosis.

Reabilitação estética multidisciplinar. Parte 2: plástica gengival, preparo do conduto, moldagem e confecção do núcleo metalocerâmico / Multidisciplinary esthetic rehabilitation. Parte 2: gingivoplasty, intraradicular preparation, impression-taking and fabrication of a metal-ceramic core

Tratamento reabilitador estético exige visão ampla durante o diagnóstico, para que se estabeleça correto plano de tratamento, obedecendo-se à ordem correta da realização de cada procedimento. Avaliação dos tecidos periodontais é necessária, não apenas considerando a relação saúde-doença, mas também a relação entre proporção dos dentes e altura do sorriso. Quando a necessidade de se realizar um procedimento periodontal é diagnosticada, este deve ser realizado, considerando-se o tempo de cicatrização e também aspectos protéticos, quando estes estão presentes. Além disso, a confecção de núcleos para reter coroas cerâmicas é uma estratégia que se deve adotar, quando o remanescente dental apresentar-se fragilizado. Este artigo, a segunda parte de três etapas, demostra a sequência de cirurgia plástica gengival, moldagem e confecção de núcleo metalocerâmico

An esthetic rehabilitation treatment should always be accompanied by a periodontal evaluation. In some cases, plastic gingival surgery is required and this procedure must be performed carefully to avoid compromising the overall treatment. Furthermore, the preparation of core for abutment crows is important when the remaining tooth is weakened. The purpose of this paper, the second of a three-part article, is to demonstrate a sequence to perform an esthetic periodontal surgery, impression-taking and metal-ceramic core

Avaliação da resistência ao cisalhamento e da durabilidade de união entre sistemas para reparo em metalocerâmicas e titânio / Evaluation of shear bond strength and bond durability of metal-ceramic repair systems and titanium

O reparo de restaurações metalocerâmicas fraturadas é uma opção de tratamento que possibilita o aumento da longevidade da restauração, preservando a estrutura dental, além de ser uma alternativa rápida e de menor custo. Entretanto, o estabelecimento de uma união forte e estável entre material reparador e substrato da restauração fraturada é essencial para o sucesso do reparo. Levando-se em consideração a grande utilidade dos reparos quando corretamente indicados e a possibilidade de um aprimoramento dos mesmos com esses novos sistemas, conforme prometem os fabricantes, foi propósito deste estudo avaliar, em titânio comercialmente puro, a resistência ao cisalhamento de quatro sistemas comerciais de reparo para metalocerâmicas e da variação de um destes, bem como a durabilidade de união após armazenamento em água. Foram confeccionados discos (9 × 3 mm) em titânio comercialmente puro. Estes foram incluídos em anel de PVC com resina acrílica e suas superfícies regularizadas com lixas de carbeto de silício de diferentes granulações (120, 220 e 320) em politriz. Os espécimes receberam um dos seguintes tratamentos (n=10): 1) Epricord, 2) Bistite II DC, 3) Cojet, 4) Scotchbond Multi Uso Plus (grupo Controle), e 5) uma variação do grupo Controle, na qual foram empregadas partículas de sílica do sistema Cojet Sand em substituição às de óxido de alumínio. Os espécimes foram armazenados em água destilada a 37ºC por 24 horas, termociclados (5.000 ciclos - 5º e 55ºC) e, então, armazenados nas mesmas condições descritas anteriormente, por um período adicional de 24 horas ou 6 meses. O ensaio de cisalhamento foi realizado em máquina de ensaios Material Test System 810 com velocidade de 0,5 mm/minuto. O modo da fratura foi avaliado em lupa estereoscópica (30x). Às 24 horas, as médias de resistência (MPa) dos grupos de 1 a 5 foram respectivamente: 13,00 + 2,04c, 8,10 + 1,16d, 18,34 + 2,16b, 13,41 + 1,42c, e 22,73 + 1,42a . Aos 6 meses, foram: 11,20 + 1,26b , 4,79 + 0,38c , 7,36 + 1,91a, 10,11 + 1,29b, e 18,55 + 1,22a . O armazenamento em água afetou significativamente a resistência de união dos grupos 2, 4 e 5, reduzindo suas resistências. Às 24 horas, a resistência ao cisalhamento da combinação Scotchbond Multi Uso/Cojet Sand foi significativamente maior em relação aos demais grupos. Aos 6 meses, o sistema Cojet e a combinação Cojet Sand/ Scotchbond Multi Uso Plus foram estatisticamente superiores aos demais grupos e iguais entre si

Repair is a good alternative treatment that can increase clinical longevity of the failed restoration, preserving tooth structure, with the advantages of less chair time and lower cost. However, the clinical success of repair depends on establishing a strong and longterm durable bond between the repair material and the metal surface of the failed restoration. Considering the great benefit of intra-oral repairs and the possibility of improvement with the use of new available repair systems, the purpose of the present study was to evaluate shear bond strength of different repair systems to commercially pure titanium (CP Ti) and bond durability after long-term water storage. One-hundred disk specimens of cast CP Ti (9 × 3 mm) were embedded in a PVC ring and their bonding surfaces were smoothed with silicon carbide papers (120, 220, and 320 grit) using a polisher. Specimens were divided into 5 groups of 20, which received one of the following repair systems: 1) Epricord, 2) Bistite II DC 3) Cojet, 4) Scotchbond Multipurpose Plus (control Group), and 5) Cojet Sand plus Scotchbond Multipurpose Plus (variation of the control Group). The specimens were stored in distilled water for 24 hours at 37ºC, thermal cycled (5,000 cycles ­ 5º to 55ºC) and then stored in distilled water at 37o C for either 24 hours or 6 months. Shear bond tests were performed in a mechanical testing machine with a crosshead speed of 0.5 mm/minute. Each specimen was examined under a stereoscopic lens with ×30 magnification. At 24 hours, the mean values (MPa) for the groups 1 to 5 were respectively 13,00 + 2,04c , 8,10 + 1,16d, 18,34 +2,16b, 13,41 + 1,42c, e 22,73 + 1,42a. After 6 months, the mean (MPa) of each group was respectively 11,20 + 1,26b , 4,79 + 0,38c, 17,36 + 1,91a , 10,11 + 1,29b e 18,55 + 1,22a. Long-term water storage significantly affected groups 2, 4, 5, which showed a significant decrease of shear bond strength. At 24 hours, Cojet Sand/Scotchbond Multipurpose Plus showed the highest shear bond strength when compared to the other four groups. After 6 months, Cojet Sand/Scotchbond Multipurpose Plus and Cojet systems were not statistically different and were statistically superior to the other groups

Avaliação da resistência à abrasão do Ti cp frente a diversos materiais restauradores / Evaluation of Wear Resistance of cp Ti Opposing Several Restorative Materials

O uso do titânio comercialmente puro (Ti cp) tem aumentado na confecção de estruturas metálicas de próteses. Assim, o objetivo deste trabalho foi avaliar in vitro a resistência à abrasão do Ti cp em oposição a diversos materiais restauradores. Foram fundidos corpos-de-prova de forma hemiesféricas (5mm de raio) em titânio cp grau I por arco voltaico em atmosfera inerte de argônio. Como antagonistas foram preparados discos com 20,0mm de diâmetro de: Ti cp; ligas de Co-Cr e Ni-Cr, resina composta TPH e cerâmica Empress-2, todos com rugosidade de 0,75 micrometro. Foram realizados aproximadamente 40000 ciclos (4,4Hz) sob carga constante de 5N. A resistência à abrasão do titânio foi medida pelo desgaste vertical dos corpos-de-prova hemiesféricos em projetor de perfil Nikon. Os dados foram submetidos à ANOVA e teste complementar de Tukey (alfa=0,05). Os resultados (micrometros) encontrados foram: Ti cp X resina (37,75±7,99); Ti cp X cerâmica (73,25±9,96); Ti cp X Co-Cr (77,17±9,95), Ti cp X Ti cp (199,00±86,90) e Ti cp X Ni-Cr (261,50±39,23). Não houve diferença significante (p>0,05) quando os antagonistas foram de resina, cerâmica e liga de Co-Cr. Quando submetido a antagonistas de Ti cp e liga de Ni-Cr os resultados foram estatisticamente significantes (p<0,05), com maior desgaste contra o antagonista de Ni-Cr. É possível concluir que o material a ser utilizado na arcada antagonista deve ser escolhido cuidadosamente quando as próteses forem confeccionadas em Ti cp porque há o risco de desgaste da prótese.

The use of commercially pure titanium (cp Ti) has increased in prosthodontics frameworks. Thus, the aim of the present study was to evaluate in vitro wear resistance of cp Ti opposing several restorative materials. Hemispheres (r=5mm) were cast in cp grade I by arc melting under inert argon atmosphere. As antagonistic samples, disks of 20mm in diameter were prepared in cp Ti, Co-Cr and Ni-Cr alloy, composite resin and Empress-2 ceramic, and roughness was adjusted to 0.75 micrometro. It was performed approximately 40,000 cycles (4.4Hz) using a load of 5N. Wear resistance of cp Ti was measured as height loss of hemispherical samples in a Nikon profile projector. The data were submitted to ANOVA and post-hoc Tukey test (alfa=0.05). The results (micrometros) were: cp Ti X composite resin (37.75±7.99); cp Ti X ceramic (73.25±9.96); cp Ti X Co-Cr (77.17±9.95), cp Ti X cp Ti (199.00±86.90) and cp Ti X Ni-Cr (261.50±39.23). No significant difference was noted (p>0.05) when antagonistic were composite resin, ceramic or Co-Cr alloy. When cp Ti opposed to cp Ti and Ni-Cr alloy, the results were statistically significant (p<0.05), presenting greater wear when Ni-Cr alloy was used as antagonist. It is possible to conclude that the material used as antagonist should be chosen carefully when titanium frameworks are used because there is a risk of wear of prostheses.

Reparo intraoral de próteses metalo-cerâmicas : um relato de caso clínico / Intraoral repair in metal-ceramic prostheses: a clinical report

Repairing fractured metal-ceramic prosthesis is a treatment alternative that can increase the restoration longevity, preserve dental structure, and/or the integrity of implant components, besides being a simple, low-cost technique. However, clinicians often see restoration repair as a challenge because of the many doubts regarding the procedures required to obtain satisfactory results. Therefore, the motivation to write this article is the need to provide instructions for clinicians dealing with a situation involving fractured porcelain, presenting an intraoral repair technique that can be used in cases of a fractured ceramic veneer of a fixed partial prosthesis. The technique consisted in treating the remaining ceramic surface and applying a microhybrid composite resin following the steps of a protocol that, according to scientific evidence, has promoted high bond strength to porcelain, in addition to being cost effective.

O reparo de próteses metaloceramicas, quando a cerâmica encontra-se fraturada, e um tratamento alternativo que pode aumentar a longevidade dessas restaurações, preservar a estrutura dental ou a integridade de componentes protéticos sobre implantes, alem de ser uma técnica simples e de baixo custo. No entanto, essa técnica, geralmente, e vista como um desafio pelos cirurgiões-dentistas uma vez que não ha um protocolo clinico bem estabelecido para a obtenção de resultados satisfatórios. Assim sendo, o objetivo deste artigo e prover instruções para os clínicos lidarem com situações de fratura da cerâmica por meio da apresentação de um caso clinico, no qual uma técnica de reparo intra-oral indicada para essa situação foi empregada. Essa técnica consiste em tratar a superfície da cerâmica remanescente e aplicar uma resina composta microhibrida, seguindo os passos de um protocolo que, de acordo com evidencias cientificas, tem promovido alta resistência de união, alem de apresentar um baixo custo.

Influência da ciclagem térmica e diferente tipos de solda na resistência da interface metalo-cerâmica / Influences of thermocycling and different kinds of weld on metal-ceramic interface resistance

O efeito da soldagem e termociclagem na união metalo-cerâmica foi avaliado pela fundição de sessenta barras metálicas em NiCr nas dimensões estabelecidas para o teste de flexão (ISO 9693:1999E). Destas, 20 barras formaram o grupo controle (GC) e 40 foram segmentadas: 20 unidas por brasagem (GB) e 20 soldadas a laser (GL). Uma camada de 1,0mm de cerâmica foi aplicada sobre as barras, as quais receberam (0,1mm de opaco e 0,9mm de dentina) na sua área central e inferior. A área total testada foi de 20mm com carga central. Os tratamentos de superfície do metal, a temperatura e tempos de queima da cerâmica foram os recomendados pelos fabricantes. A metade dos corpos-de-prova foi termociclada (GCT, GBT e GLT). Todos os corpos-de-prova foram submetidos ao teste de flexão de três pontos com célula de carga de 10Kg e velocidade 1,5±0,5mm/min em uma máquina de ensaios universal, e as cargas máximas até a falha inicial foram anotadas. Os dados foram submetidos à análise de variância e ao teste de Tukey. Não houve diferença significante estatisticamente com relação à força máxima até a falha de união metalo-cerâmica para os grupos GB (10,55±1,37N), GL (9,87±1,22N) e grupo controle GC (14,5±2,11N), que apresentou a força mais alta até falha, estatisticamente significante em relação aos demais grupos, com p=0,001. Para a termociclagem, não houve diferença significativa estatisticamente dentro de todos os grupos estudados. Após o teste, um corpo-de-prova de cada um dos grupos, foi observado por MEV associado ao EDX.

Among these ones, 20 bars formed the control group (CG) and 40 were divided: 20 were attached by the use of brazing (BG) and 20 were laser welded (LG). A 1,0mm ceramic layer (0,1mm of opaque ceramics and 0,9mm of dentine ceramics) was applied over the bars, on its central and bottom area. The total area tested had 20mm2, with central load. The metal surfaces treatments, the temperature, and the times of ceramics coccion were recommended by the manufacturers. Half of the specimens were thermocycled (CGT, BGT, LGT). All the specimens underwent the three point bending test with a 10-kilo load cell and speed of 1,5±0,5mm/min in an universal testing machine and the maximum load up to initial failure was marked. Data underwent statistical analysis (ANOVA and Tukey Test). There was no relevant static difference concerning the maximum load to metal-ceramic failure of the groups BG (10,55±1,37N) and LG (9,87±1,22N), but CG had the highest load up to failure (14,5±2,11N), statistically relevant, of all the groups, with p=0,001. When it comes to thermocycling, there were no relevant differences statistically, among all the studied groups. After the test, one specimen of each one of the groups was observed by MEV associated to EDX.